GDP storage tank edge plate waterproof elastic glue
I. Overview
Corrosion-resistant and waterproof elastic rubber is a nano-level high-elasticity and corrosion-resistant material obtained by modifying silicone rubber, hydrogenated nitrile rubber and other synthetic polymer materials. The material has outstanding viscoelasticity, certain tensile strength, excellent adhesion, good chemical resistance and UV aging resistance. The material is a two-component system, which is easy to use. By adding a composite flame retardant, a good flame retardant effect can be achieved. This product is mainly used in military and nuclear industry facilities. It is also used in other occasions with special requirements.
Corrosion-resistant and waterproof elastic glue is formulated into an elastic clay layer, which can greatly improve the impact resistance and damping of the coating, and can effectively resist the changes in the outer edge of the large oil tank and the vibration during operation. The resulting coating cracks.
For specific construction technology, please refer to the construction technical plan manual provided by our company.
Technical performance table of GDP corrosion-resistant waterproof elastic glue
Project | Unit | Index | Testing standard |
proportion | g.cm-3 | 1.5-1.6 | GB1756 |
Tensile Strength | MPa | ≥4.5 | GB/T1040.2-2006 |
Elongation | % | ≥300 | |
Bonding strength with concrete | MPa | ≥9.0 | GB/T2792-2014 |
Bonding strength with steel plate | MPa | ≥5.0 | |
Shear strength with steel plate | MPa | ≥0.3 | |
Impermeable | 0.3MPa、30分钟 | impermeable | GB1037-1988 |
Drying time | hour | Surface dry≤6、Hard work≤24 | GB/T16777-2008 |
Tensile fatigue resistance | 0.3MPaNumber of reciprocating stretching | ≥10000 | GB/T23257-2009 appendixH |
Heat treatment（80℃，168h） | Tensile strength retention rate（%） | 90～150 | |
Elongation at break（%） ≥ | 650 | ||
Low temperature bending（℃） ≤ | -40 | ||
Alkali treatment（0.1%NaOH+saturationCa(OH)2Solution，168h) | Tensile strength retention rate（%） | 70～140 | |
Elongation at break（%） ≥ | 550 | ||
Low temperature bending（℃） ≤ | -40 | ||
Acid treatment（2%H2SO4Solution，168h） | Tensile strength retention rate（%） | 70～150 | |
Elongation at break（%） ≥ | 550 | ||
Low temperature bending（℃） ≤ | -40 | ||
Artificial weathering（1000h） | Tensile strength retention rate（%） | 90～150 | GB/T23257-2009 appendix I |
Elongation at break（%） ≥ | 550 | ||
Low temperature bending（℃） ≤ | -40 | ||
500uvDirect UV high pressure mercury lamp | No chalking or cracking of the coating film | ||
Salt spray resistance（500h） | No bubbles, no cracks, no delamination | GB/T1771 |
2. Product features
1. The waterproof layer is formed into a film by applying several layers of elastic glue and then solidly drying, without lap joints and gaps;
2. The adhesion and peeling strength of the waterproof adhesive layer to the tank wall and cement surface is high;
3. The gap and transition between the bottom plate and the cement platform are preset with a triangular permanent elastic buffer layer similar to the glue layer, which can effectively dampen the expansion vibration of the edge plate;
4. The brushing process is cold coating operation, and no fire is required;
5. Good weather resistance and high elastic elongation, guaranteeing a period of over eight to ten years.